Nickel Chromium NiCr Alloy
Materiae Nickel-chromium late adhibentur in fornacibus electricis industrialibus, subsidiis domesticis, machinationibus remotis aliisque instrumentis ob excellentem caliditatem virium et validam plasticitatem. Nickel-chromium et ferrum, aluminium, pii, carbonum, sulphur et alia elementa in filum alloyamentum nickel-chromium fieri possunt, quae magno resistivity et calore resistit et est elementum calefactionis electricae fornacis electrici, ferrum electrici solidarii, ferri electrici et electrici. alias producta.
Praeterea filum NiCr in coil lapsae rheostat adhiberi solet, ut circumitionem tuendam et mutationem currentem in gyro mutando resistat accessus ambitus partis, inde transverso conductore (electrica appliance) mutata intentione in serie cum connexo. illud, quod frequentes adjumenta suppeditant.
NiCr Alloy Series
Ni90Cr10 habena est genus of nigel-chromium mixturae productorum, idoneus est ad applicationes temperaturas usque ad 1250°C. Chromium contentus praebet tempus vitae valde bonae, uti solet elementum calefactionis vape.
Ni90Cr10 notatur magna resistentia, oxidatio bona resistentiae, ductilis bona post usum et optimae coniugii. NiCr Alloy materia bona est industriae calefaciendi.
Ni90Cr10 Nickel-Chromium Nickel NiCr Alloy resistentia calefactio claua
Nickel-chromium Alaymus NiCr Alloy perficientur tables
| NiCr Alloy euismod materia | Cr10Ni90 | Cr20Ni80 | Cr30Ni70 | Cr15Ni60 | Cr20Ni35 | Cr20Ni30 | |
| Compositio | Ni | 90 | Requiem | Requiem | 55.0～61.0 | 34.0～37.0 | 30.0～34.0 |
| Cr | 10 | 20.0～23.0 | 28.0～31.0 | 15.0～18.0 | 18.0～21.0 | 18.0～21.0 | |
| Fe |
| ≤1.0 | ≤1.0 | Requiem | Requiem | Requiem | |
| Maximum temperatus℃ | 1300 | 1200 | 1250 | 1150 | 1100 | 1100 | |
| punctum liquescens | 1400 | 1400 | 1380 | 1390 | 1390 | 1390 | |
| Densitas g/cm3 | 8.7 | 8.4 | 8.1 | 8.2 | 7.9 | 7.9 | |
| Resistentia |
| 1.09±0.05 | 1.18±0.05 | 1.12±0.05 | 1.00±0.05 | 1.04±0.05 | |
| μΩ·m,20℃ | |||||||
| Prolongatio ad rupturam | ≥20 | ≥20 | ≥20 | ≥20 | ≥20 | ≥20 | |
| Imprimis calor |
| 0.44 | 0.461 | 0.494 | 0.5 | 0.5 | |
| J/g.℃ | |||||||
| Scelerisque conductivity |
| 60.3 | 45.2 | 45.2 | 43.8 | 43.8 | |
| KJ/mh℃ | |||||||
| Coefficiens linearum expansio |
| 18 | 17 | 17 | 19 | 19 | |
| a×10-6/ | |||||||
| (20~1000) | |||||||
| Micrographic structure |
| Austenite | Austenite | Austenite | Austenite | Austenite | |
| Magnae possessiones |
| Nonmagnetic | Nonmagnetic | Nonmagnetic | Debilis magneticus | Debilis magneticus | |